Calcium Fluoride (CaF₂) is commonly used for optics looking at the IR and UV spectrums and has a very low change in refractive index with wavelength.
| Material | Calcium Fluoride |
| Diameter Tolerance | +0.0/-0.1 mm |
| Thickness Tolerance | ±0.1 mm |
| Parallelism | 1 arc min |
| Surface Quality | 60-40 Scratch-Dig |
| Surface Flatness (Plano Side) | λ/2 at 633nm |
| Surface Irregularity (Peak to Valley) | λ/2 at 633nm |
| Clear Aperture | 90% |
| Chemical Formula | CaF2 |
| Crystal Class | Cubic, cleaves [111] plane |
| Lattice Constant, Å | 5.46 |
| Density, g/cm3 (20 °C) | 3.18 |
| Molecular Weight | 78.08 |
| Reflection Loss | 5.4% at 5 μm |
| Absorption Coefficient | 7.8 x 10-4 cm-1 @ 2.7 μm |
| Dielectric Constant for 105 Hz | 6.76 |
| Melting Temperature, K | 1630 |
| Thermal Conductivity, W/(m K) at 273 K | 10 |
| Thermal Expansion, 1/K at 300 K | 18.9 x 10-6 |
| Specific Heat, cal/(g K) at 273 K | 0.204 |
| Debye Temperature, K | 510 |
| Young's Modulus, GPa | 75.79 |
| Rupture Modulus, GPa | 0.0365 |
| Shear Modulus, GPa | 33.76 |
| Bulk Modulus, GPa | 83.03 |
| Poisson's Ratio | 0.28 |
| Knoop Hardness, kg/mm2 | 178 [100], 160 [110] |